Mechanical and Optical Properties of Waterborne UV Curing Coating Modified by Silica

DOI

10.2991/icmse-16.2016.61How to use a DOI?

Keywords

Modification, Waterborne UV wood coating, Mechanical, Gloss

Abstract

Silica (SiO2) was used to modify the waterborne ultraviolet (UV) curing wood coatings, and the waterborne UV curing wood coating was prepared by optimizing the process parameters. The mechanical properties of the waterborne UV curing wood coating (hardness, adhesion and impact strength) and gloss were tested. When the SiO2 content in the waterborne UV curing wood coating was 3%, the waterborne UV curing wood coatings was drying at 40øC for 30 min in the oven firstly, then irradiated with UV lamp for 1 min, the obtained waterborne UV curing wood coating had good hardness, adhesion and impact strength. However, when SiO2 content of waterborne UV curing wood coating was more than 3%, the mechanical properties decreased. The gloss test showed that the gloss of waterborne UV curing wood coating was elevated with the decreased content of SiO2. When the SiO2 content was higher than 3%, the gloss of waterborne UV curing wood coating exhibited matt.

Copyright

© 2016, the Authors. Published by Atlantis Press.

Open Access

This is an open access article distributed under the CC BY-NC license (http://creativecommons.org/licenses/by-nc/4.0/).

Download article (PDF)

TY  - CONF
AU  - Xiao-Xing Yan
AU  - Yun-Ting Cai
AU  - Guo-Yue Xu
AU  - Wei Xu
PY  - 2016/12
DA  - 2016/12
TI  - Mechanical and Optical Properties of Waterborne UV Curing Coating Modified by Silica
BT  - Proceedings of the 4th 2016 International Conference on Material Science and Engineering (ICMSE 2016)
PB  - Atlantis Press
SP  - 370
EP  - 375
SN  - 2352-5401
UR  - https://doi.org/10.2991/icmse-16.2016.61
DO  - 10.2991/icmse-16.2016.61
ID  - Yan2016/12
ER  -