A novel high water-resistant aqueous acrylate emulsion, part 1: preparation and characterization

DOI

10.2991/peee-15.2015.13How to use a DOI?

Keywords

Fluorinated acrylate, Aqueous emulsion, Core-shell structure, Water-resistance, Uniform particle size

Abstract

The acrylate copolymer emulsion with core-shell structure was successfully prepared via pre-emulsified semi-continuous seeded polymerization using SDS and OP-10 as compound emulsifier, and methyl methylacrylate (MMA), butyl acrylate (BA) and dodecafluoroheptyl methacrylate (DFMA) as main monomers. SEM and OCA were used to characterize the structure and the product, meanwhile, the influence of core-shell monomer ratio, the dosage of emulsifier, initiator and fluoride monomers on the reacting product properties were studied. Obvious ball structure could be seen clearly by the scanning electron microscopes when the hard monomer MMA matched with a moderate amount of DFMA as the shell in an optimized reaction condition. Detected with the help of particulate size description analyser, the latex particle which had uniformly size was found mono-dispersed.

Copyright

© 2015, the Authors. Published by Atlantis Press.

Open Access

This is an open access article distributed under the CC BY-NC license (http://creativecommons.org/licenses/by-nc/4.0/).

Download article (PDF)

TY  - CONF
AU  - B.K. Ren
AU  - K.T. Hu
AU  - G.H. Li
AU  - A.B. Wu
AU  - J.J. Li
PY  - 2015/04
DA  - 2015/04
TI  - A novel high water-resistant aqueous acrylate emulsion, part 1: preparation and characterization
BT  - Proceedings of the 2015 International Conference on Power Electronics and Energy Engineering
PB  - Atlantis Press
SP  - 51
EP  - 54
SN  - 2352-5401
UR  - https://doi.org/10.2991/peee-15.2015.13
DO  - 10.2991/peee-15.2015.13
ID  - Ren2015/04
ER  -