Effect of Anneal Temperature on Microstructure and Mechanical Properties of 0Cr21Ni6Mn9N cold Drawn Pipe

DOI

10.2991/ame-16.2016.64How to use a DOI?

Keywords

Austenitic Stainless Steel, Cold Drawn Pipe, Mechanical Properties, Recrystallization, Precipitation.

Abstract

The microstructure and mechanical properties of 0Cr21Ni6Mn9N austenitic stainless steel cold drawn pipe were investigated at various annealing temperatures. It was found that the tensile strength and the yield strength increased slightly, and then decreased with the temperature increasing from 200 to 750 °C. The highest value of tensile strength and yield strength reached 1062 and 942MPa at 600 °C, respectively. However, the elongation has an opposite trend to the tensile strength and yield strength. The microstructure evolution of the cold drawn pipe annealed at different temperatures was observed. The results indicate that when annealed below 550 °C, recovery is dominant. At 550 °C, it is recovery and partial recrystallization. Over 550 °C, complete recrystallization has likely occurred. Moreover, the Cr2N particles near the grain boundaries were found, and the amount of precipitates along the grain boundary indexed as M23C6 were increasing at 650-800 °C.

Copyright

© 2016, the Authors. Published by Atlantis Press.

Open Access

This is an open access article distributed under the CC BY-NC license (http://creativecommons.org/licenses/by-nc/4.0/).

Download article (PDF)

TY  - CONF
AU  - L.L. Xiong
AU  - H.Z. Zheng
AU  - F.W. Yuan
AU  - S.Q. Lu
AU  - Q.H. Luo
PY  - 2016/06
DA  - 2016/06
TI  - Effect of Anneal Temperature on Microstructure and Mechanical Properties of 0Cr21Ni6Mn9N cold Drawn Pipe
BT  - Proceedings of the 2nd Annual International Conference on Advanced Material Engineering (AME 2016)
PB  - Atlantis Press
SP  - 387
EP  - 393
SN  - 2352-5401
UR  - https://doi.org/10.2991/ame-16.2016.64
DO  - 10.2991/ame-16.2016.64
ID  - Xiong2016/06
ER  -