Effect of Cold Plasma Treatment on FRP Surface: The Behavior of FRP/Wood Interfacial Adhesion

Authors
Yuan Hui, Shen Shijie, Qiu Chen, Zhao Shuping
Corresponding Author
Yuan Hui
Available Online September 2015.
DOI
10.2991/iea-15.2015.18How to use a DOI?
Keywords
G-FRP; plasma treatment; glulam; interfacial adhesion; delamination properties; shear strength; fracture toughness
Abstract

In this work, FRP panel surface was treated by 12 plasma techniques formed by a pairwise combination of four power consumptions (300W, 400W, 500W, and 600W) and three transmission velocity (2.5m/min, 5.0m/min, and 7.5m/min) respectively, and then adhere to timbers. According to delamination test dates, 7 of 12 specimen groups meet the requirement. Shear strength at dry state of composite – FRP/wood –was improved. Mode GIIC of 4ENF for the composite fracture toughness test was inferred in this paper. Variance analysis results demonstrated that power and velocity interaction has significant influence on delamination properties of FRP-wood interface, and power has significant influence on shear strength and fracture toughness. Considering strength and toughness synthetically, the optimized process of plasma treatment on FRP surface could be concluded, which power consumption was 300W, transmission speed was 5.0m/min. With this process, the properties of the composite interface are as following: the average shear strength at dry state was 9.46MPa, 6.49MPa at wet state, the GIIC was 0.94kJ/m2, and the average delamination ratio was 1% and 3% after soaked in normal and boiling water, which are all meet the request of standard.

Copyright
© 2015, the Authors. Published by Atlantis Press.
Open Access
This is an open access article distributed under the CC BY-NC license (http://creativecommons.org/licenses/by-nc/4.0/).

Download article (PDF)

Volume Title
Proceedings of the AASRI International Conference on Industrial Electronics and Applications (2015)
Series
Advances in Engineering Research
Publication Date
September 2015
ISBN
978-94-62520-65-3
ISSN
2352-5401
DOI
10.2991/iea-15.2015.18How to use a DOI?
Copyright
© 2015, the Authors. Published by Atlantis Press.
Open Access
This is an open access article distributed under the CC BY-NC license (http://creativecommons.org/licenses/by-nc/4.0/).

Cite this article

TY  - CONF
AU  - Yuan Hui
AU  - Shen Shijie
AU  - Qiu Chen
AU  - Zhao Shuping
PY  - 2015/09
DA  - 2015/09
TI  - Effect of Cold Plasma Treatment on FRP Surface: The Behavior of FRP/Wood Interfacial Adhesion
BT  - Proceedings of the AASRI International Conference on Industrial Electronics and Applications (2015)
PB  - Atlantis Press
SP  - 67
EP  - 71
SN  - 2352-5401
UR  - https://doi.org/10.2991/iea-15.2015.18
DO  - 10.2991/iea-15.2015.18
ID  - Hui2015/09
ER  -