The effect in the production and Luminescence property of Zn3V2O8 with fluxing
Jiaolian Luo, Weifu Cen, Xiaoming Zhang, Shilin Yu, Ruxue Chen, Zhenglin Zhou, Yingfu Zhang, Ting Huang
Available Online September 2016.
- https://doi.org/10.2991/iccia-16.2016.63How to use a DOI?
- Zn3V2O8; High temperature solid phase synthesis technique; Photo-luminescence; Flux; Crystal structure.
- The sample of Zn3V2O8 has been preparation by high temperature solid phase method with fluxing, and studied the effect of preparation condition and the luminescence property with fluxing. The results of phase studied show that the crystal morphology was improved, the reunite of grain crystal was decreased, and the effect of crystal structure was none by fluxed. The results of luminescence property shows that the emission peak was appeared at the wave-length of 400—700 nm, and the highest peak appeared at the wave-length of 550nm under the near ultraviolet excitation light of 360nm, the results shows that the luminescence property was improved by flux of NH4Cl, NH4F and H3BO3.
- Open Access
- This is an open access article distributed under the CC BY-NC license.
Cite this article
TY - CONF AU - Jiaolian Luo AU - Weifu Cen AU - Xiaoming Zhang AU - Shilin Yu AU - Ruxue Chen AU - Zhenglin Zhou AU - Yingfu Zhang AU - Ting Huang PY - 2016/09 DA - 2016/09 TI - The effect in the production and Luminescence property of Zn3V2O8 with fluxing BT - 2016 International Conference on Computer Engineering, Information Science & Application Technology (ICCIA 2016) PB - Atlantis Press SP - 343 EP - 347 SN - 2352-538X UR - https://doi.org/10.2991/iccia-16.2016.63 DO - https://doi.org/10.2991/iccia-16.2016.63 ID - Luo2016/09 ER -